ASTM A403 Standard Specification

ASTM A403 Standard specification covers the standard for wrought austenitic stainless steel fittings for pressure piping applications. ASTM A403 / A403M Standard Specification for Wrought Austenitic Stainless Steel Piping Fittings.

A403 WP304L Pipe Fittings

ASTM A403 WPL6 Elbow after complete quality and performance measure inspection. These are widely appreciated for excellent quality, corrosion abrasion and high tensile strength with long life service.

The material for fittings shall consist of forgings, bars, plates, or seamless or welded tubular products. Forging or shaping operations shall be performed by hammering, pressing, piercing, extruding, upsetting, rolling, bending, fusion welding, machining, or by a combination of two or more of these operations. All fittings shall undergo heat-treatment. Chemical and product analyses shall be performed and shall conform to the required chemical composition in carbon, manganese, phosphorus, sulfur, silicon, chromium, molybdenum, and titanium. Tension test shall be done on the fitting material to determine the tensile properties such as yield strength and tensile strength. Fittings supplied under this specification shall be examined visually for surface discontinuities, surface checks, and mechanical marks.

This abstract is a brief summary of the referenced standard. It is informational only and not an official part of the standard; the full text of the standard itself must be referred to for its use and application. ASTM does not give any warranty express or implied or make any representation that the contents of this abstract are accurate, complete or up to date.

Wrought Austenitic Stainless Steel Piping Fittings

Materials shall consist of forgings, bars, plates, seamless or fusion welded tubular products with filler metal added, and shall be produced by open-hearth, basic-oxygen, or electric-furnace process. Forging or forming operations shall be performed by one or a combination of two or more of the following procedures: hammering, pressing, piercing, extruding, upsetting, working, bending, fusion-welding, or machining. All welding shall be completed prior to the austenitizing heat treatment, which shall be executed in the normalized, normalized and tempered, annealed, or quenched and tempered conditions. Steel specimens shall conform to required values of chemical composition, tensile strength, yield strength, elongation, wall thickness, and Charpy V-notch impact value. All fusion-welded butt joints shall undergo radiographic examination, while hydrostatic testing of fittings is not required in this specification. Repair welding shall be permissible for parts made to dimensional standards.

Fitting Classes for WP Grades

This abstract is a brief summary of the referenced standard. It is informational only and not an official part of the standard; the full text of the standard itself must be referred to for its use and application. ASTM does not give any warranty express or implied or make any representation that the contents of this abstract are accurate, complete or up to date.

Referenced Documents

ASTM Standards
  • A216/A216M Specification for Steel Castings, Carbon, Suitable for Fusion Welding, for High-Temperature Service
  • A217/A217M Specification for Steel Castings, Martensitic Stainless and Alloy, for Pressure-Containing Parts, Suitable for
High-Temperature Service
  • A960/A960M Specification for Common Requirements for Wrought Steel Piping Fittings
ASME Standards
  • B16.11 Forged Steel Fittings, Socket Welding and Threaded
  • ASME Boiler and Pressure Vessel Code
  • SectionIX Welding Qualifications
MSS Standards
  • MSS-SP-95 Swage(d) Nipples and Bull Plugs

Scope of ASTM A403

1.1 This specification covers wrought carbon steel and alloy steel fittings of seamless and welded construction, covered by the latest revision of ASME B16.9, ASME B16.11, MSS SP-79, MSS SP-83, MSS SP-95, and MSS SP-97. Fittings differing from these ASME and MSS standards shall be furnished in accordance with Supplementary Requirement S58 of Specification A960/A960M. These fittings are for use in pressure piping and pressure vessel service at low temperatures.

1.2 Optional supplementary requirements are provided for fittings where a greater degree of examination is desired. When desired, one or more of these supplementary requirements shall be specified in the order.

1.3 This specification is expressed in both inch-pound units and in SI units. However, unless the order specifies the applicable “M” specification designation (SI units), the material shall be furnished to inch-pound units.

1.4 The values stated in either SI units or inch-pound units are to be regarded separately as standard. Within the text, the SI units are shown in brackets. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in non-conformance with the standard.

Chemical Composition (%) of ASTM A403
Steel No. Type Chemical composition
C Si S P Mn Cr Ni Mo Other ób ós δ5
WP304 0.08 1 0.03 0.045 2 18-20 8-11 515 205 28
WP304H 0.04-0.1 1 0.03 0.045 2 18-20 8-11 515 205 28
WP304L 0.035 1 0.03 0.045 2 18-20 8-13 485 170 28
WP304LN 0.03 0.75 0.03 0.045 2 18-20 8-10.5 N2:0.1-0.16 515 205 28
WP304N 0.08 0.75 0.03 0.045 2 18-20 8-11 N2:0.1-0.16 550 240 28
WP309 0.15 1 0.03 0.045 2 22-24 12-15 515 205 28
WP310 0.15 1.5 0.03 0.045 2 24-26 19-22 515 205 28
WP316 0.08 1 0.03 0.045 2 16-18 10-14 2-3 515 205 28
WP316H 0.04-0.1 1 0.03 0.045 2 16-18 10-14 2-3 515 205 28
WP316LN 0.03 0.75 0.03 0.045 2 16-18 11-14 2-3 N2:0.1-0.16 515 205 28
WP316L 0.035 1 0.03 0.045 2 16-18 10-16 2-3 485 170 28
WP316N 0.08 0.75 0.03 0.045 2 16-18 11-14 2-3 N2:0.1-0.16 550 240 28
WP317 0.08 1 0.03 0.045 2 18-20 11-15 3-4 515 205 28
WP317L 0.03 1 0.03 0.045 2 18-20 11-15 3-4 515 205 28
WP321 0.08 1 0.03 0.045 2 17-20 9-13 Ti:5C-0.7 515 205 28
WP321H 0.04-0.1 1 0.03 0.045 2 17-20 9-13 Ti:4C-0.7 515 205 28
WP347 0.08 1 0.03 0.045 2 17-20 9-13 Nb+Ta:10C-1.1 515 205 28
WP347H 0.04-0.1 1 0.03 0.045 2 17-20 9-13 Nb+Ta:8C-1 515 205 28
WP348 0.08 1 0.03 0.045 2 17-20 9-13 Ta:0.1 515 205 28
WP348H 0.04-0.1 1 0.03 0.045 2 17-20 9-13 Ta:0.1 515 205 28

Notes:

  • For each reduction of 0.01% below the specified C maximum, an increase of 0.06% Mn above the specified maximum will be permitted, up to a maximum of 1.35%.
  • The sum of Cu, Ni, Cr, and Mo shall not exceed 1.00%.
  • The sum of Cr and Mo shall not exceed 0.32%.
  • The maximum carbon equivalent (C.E.) shall be 0.50, based on heat analysis and the formula C.E.=C+Mn/6+(Cr+Mo+V)/5+(Ni+Cu)/15.

Material Furnished to this specification shall conform to the requirements of specifications A960/A960M including any supplementary requirements that are indicates in the purchase order . Failure to company with the common requirements of Specification A960/A960M constitutes non-conformance with this specification . In case of conflict between this specification and Specification A960/A960M , this specification shall prevail .

Get in touch

Welcome to Sunny Steel Enterprise Ltd.

Sunny Steel provide a wide range of steel products as Steel pipes, Seamless tube and seamless pipes, Alloy pipes, Pipe fittings, Composite steel pipe used in the industry, construction etc.


Contact Form

Name

Email *

Message *

Popular posts from this blog

Barred Tee

Image
A barred tee is a tee or any fitting with a branch used in pipelines that is pigged and has a restriction bar welded internally preventing the pig from traveling down a branch connection. Barred tee is a pipe fitting that is used in a pig launcher or receiver system in a piping system to ensure the pig could pass the branch safely. Design considerations for barred tee The barred tee will be used when there is a requirement for pigging. Thus, many of its applications can be found in the pipeline or in the subsea field. The bar plates that welded internally at the branch are to avoid the pig from changing direction or getting stuck at the branch outlet. The design of the bar plates must be in sufficient quantity, thickness and adequately spaced to ensure the smoothness for the pig to run through the main pipe, and at the same time not affecting the flow that was meant to flow through the branch. Normal practice is to ensure that the opening in the branch pipeline after gui...
Read more

How to Calculate a Pipe Bend?

Image
Pipe fittings are necessary to join together pipes, or to change the direction of an existing pipe. Pipes and pipe fittings are made of a variety of materials, depending on the fluid or gas being transported. Most pipe fittings tend to be either threaded or able to slip over the pipes they connect. Whether you are using steel pipes of PVC pipes, a chemical solvent is required to create a seal between the pipe and the fittings. Measure the required length of the pipe to be installed, keeping in mind the extra length required where the pipe will be inserted into the fitting. Mark this length on the pipe. How to Calculate a Pipe Bend Whether you are bending pipe for running electrical conduit or a metal project, calculating the bend for the start and end point can be an important factor. While there are different types of pipe benders on the market, they all share a common identification for the operation. Identified on all pipe benders is the size of pipe the unit will bend alon...
Read more

ANSI Flange Standards

Image
The American National Standard Institute, ANSI, has been overseeing guidelines and standards for products manufactured through several sectors. WHAT IS ANSI? ANSI-approved flanges are used for the industrial market which handles gas, air and steam process systems. Originally formed in 1918, the American National Standards Institute is headquartered in Washington, DC, and is widely recognized as the American organization responsible for overseeing the national standards and conformity assessment system for products, services, processes, systems, and personnel. ANSI works domestically with American government agencies and organizations, as well as with international entities, to make ANSI standards useful around the world. Prior to the creation of ANSI, standards for engineering and equipment such as flanges were developed by the American Institute of Electrical Engineers (AIEE or IEEE), the American Society of Mechanical Engineers (ASME), the American Institute of Mi...
Read more